As the in-service strength of Advanz™ 6CM – s300 is significantly higher than normal 5xxx alloys, this provides significantly higher energy absorption during crush. All values listed are typical.

Temper	UTS (Rm)	YS (Rp0.2)	Total Elongation A80
T4 Delivery	≥170 MPa	≤85 MPa	≥24%
2% pre-strain + 20 min @185°C	240 MPa	185 MPa	16%
2% pre-strain + 20 min @205°C	225 MPa	170 MPa	16%
T61 Delivery	≥260 MPa	≥200 MPa	≥18%
T61 2% pre-strain + 20 min @185°C	273 MPa	240 MPa	15%

The chemical composition of this product corresponds to AA6014.

Si	Fe	Cu	Mn	Mg	Cr
0.30 - 0.6	≤ 0.35	≤ 0.25	0.05 - 0.20	0.40 - 0.8	≤ 0.20
Zn	Ti	V	Others, each	Others	Other, total
≤ 0.10	≤ 0.10	0.05* - 0.20	≤ 0.05	N/A	≤ 0.15

*Only in European production of this product

Density	2.7 x 10³ kg/m³
Elastic Modulus	70,000 N/mm²
Coefficient of Thermal Expansion	23.4 x 10-6 K-1
Thermal Conductivity	160 – 190 W/mK
Electrical Conductivity	26 – 30 m/Ωmm²

Our manufacturing footprint allows us to tailor solutions for auto-makers around the world. Novelis Advanz™ 6CM – s300 is produced in the following locations:

Asia

Europe

Acid Etch TiZr PT3 AlubVs Mp-404 RP4107 E1 DC290 61-AUS/6130

Acid Etch TiZr A951 AlubVs Mp-404 RP4107 E1

Additional services may be available through our distributors, please contact your Novelis sales representative for more information.

Cut-to-length Laser Blank

All the standard finishing operation

Additional services may be available through our distributors, please contact your Novelis sales representative for more information.

0.9 - 3.0 mm

0.9 - 3.0 mm

Please contact your Novelis sales representative for more information about available widths and gauges.