The product shows good formability and bake hardening response. Due to its superior in-service strength, this alloy is ideal for down-gauging structure components. All values listed are typical.

Temper	UTS (Rm)	YS (Rp0.2)	Total Elongation A80
T4 Delivery (s)	≥235 MPa	≤120 MPa	≥2%
2% pre-strain, 20 min @ 185 ºC (e)	≥235 MPa	≤120 MPa	≥2%

The composition of e600 is within the composition of AA6451. Composition below is not 100% confirm to AA6451

Si	Fe	Cu	Mn	Mg	Cr
0.60 - 1.0	≤ 0.35	≤ 0.20	0.05 - 0.20	0.40 - 0.8	≤ 0.10
Zn	Ti	V	Others, each	Others	Other, total
≤ 0.15	≤ 0.05	N/A	≤ 0.05	N/A	≤ 0.15

Density	2.7 x 10³ kg/m³
Elastic Modulus	70,000 N/mm²
Coefficient of Thermal Expansion	23.4 x 10-6 K-1
Thermal Conductivity	160 – 190 W/mK
Electrical Conductivity	26 – 30 m/Ωmm²

Our manufacturing footprint allows us to tailor solutions for auto-makers around the world. Novelis Advanz™ 6HS – s600 is produced in the following locations:

Asia

Europe

North America

Acid Etch TiZr PT3 AlubVs Mp-404 RP4107 E1 DC290 61-AUS/6130

Acid Etch TiZr PT3 AlubVS E1 PL39SX EDT

Acid Etch TiZr A951 B2 (in development) AlubVs Mp-404 RP4107 E1

Additional services may be available through our distributors, please contact your Novelis sales representative for more information.

Cut-to-length Laser Blank

Cut-to-length Laser Blank Edge Trimming Slitting

Edge Trimming Slitting

Additional services may be available through our distributors, please contact your Novelis sales representative for more information.

0.9 -3.0 mm

0.9 -3.0 mm

0.9 -3.0 mm

Please contact your Novelis sales representative for more information about available widths and gauges.