The product shows excellent formability and bake hardening response. Due to its superior in-service strength, this alloy is ideal for down-gauging both skin and structure components. All values listed are typical.

Temper	UTS (Rm)	YS (Rp0.2)	Total Elongation A80
T4 Delivery	≥240 MPa	≤135 MPa	≥27%
2% pre-strain + 20 min @185°C	≥300 MPa	≤230 MPa	≥20%
No pre-strain, 30 min @225°C	≥320 MPa	≥285 MPa	≥12%
T6 no pre-strain, 10 hours @180°C	≥345 MPa	≥315 MPa	≥13%

The chemical composition of this product corresponds to AA6111.

Si	Fe	Cu	Mn	Mg	Cr
0.60 - 1.1	≤ 0.40	0.50 - 0.90	0.10 - 0.45	0.50 - 1.0	≤ 0.10
Zn	Ti	V	Others, each	Others	Other, total
≤ 0.15	≤ 0.10	N/A	≤ 0.05	N/A	≤ 0.15

Density	2.7 x 10³ kg/m³
Elastic Modulus	70,000 N/mm²
Coefficient of Thermal Expansion	23.4 x 10-6 K-1
Thermal Conductivity	160 – 190 W/mK
Electrical Conductivity	26 – 30 m/Ωmm²

Our manufacturing footprint allows us to tailor solutions for auto-makers around the world. Novelis Advanz™ 6HS – s615 is produced in the following locations:

Asia	North America

Acid Etch TiZr PT3 AlubVs Mp-404 RP4107 E1 DC290 61-AUS/6130 EDT

Acid Etch TiZr A951 AlubVs Mp-404 RP4107 E1

Additional services may be available through our distributors, please contact your Novelis sales representative for more information.

Cut-to-length Laser Blank

Edge Trimming Slitting

Additional services may be available through our distributors, please contact your Novelis sales representative for more information.

0.7 - 4.0 mm

0.7 - 4.0 mm

Please contact your Novelis sales representative for more information about available widths and gauges.